SC 1400
CARACTÉRISTIQUES
- Résistance chimique supérieure
- Excellente résistance à la déformation
- Aucun vieillissement
- Bonne compressibilité
- Etanchéité pour une large gamme de P et T
- Aucune reprise d’humidité
- Ininflammable
- Maintenance facilité (assemblage / démontage)
- Conforme aux spécifications FDA
- Certifié BAM (200°C, 25 bar)
- Conforme à la TA-Luft VDI 2240
Propriétés
| Property | Unit | Method | Value |
|---|---|---|---|
| Pressure, max | bar | / | 85 |
| Temperature, min | °C | / | -200 |
| Temperature, max | °C | / | 260 |
| P x T, max | bar x °C | / | 12000 |
| Density | g/cm3 | ASTM D792 | 2.2 |
| Compression Modulus Room Temperature - 20 Mpa KSW | % | DIN 28090-2 | 8 |
| Modulo di Compressione 150°C - 20 Mpa - 16 ore WSW | % | DIN 28090-2 | 3 |
| Creep Relaxation Room Temperature - 1 Mpa KRW | % | DIN 28090-2 | 15 |
| Compression Modulus 150°C - 20 Mpa - 16 hours WSW | % | DIN 28090-2 | 4 |
| Recovery | mm | DIN 28090-2 | 0.07 |
| Leakage Rate with nitrogen N2, 40bar, 32 N/mm2 | mg/s/m | DIN 28090-2 | < 0,01 |
| Leakage Rate with nitrogen N2, 40bar, 32 N/mm2 | cm3 /min | DIN 3535 | 0.02 |
| Compression Creep 150°C - 30 N/mm2 | N/mm2 | DIN 52913 | 16.5 |
| Compression Creep 175°C - 50 N/mm2 | N/mm2 | DIN 52913 | 29 |
PROPRIÉTÉS
| Property | Unit | Method | Value |
|---|---|---|---|
| Pressure, max | bar | / | 85 |
| Temperature, min | °C | / | -200 |
| Temperature, max | °C | / | 260 |
| P x T, max | bar x °C | / | 12000 |
| Density | g/cm3 | ASTM D792 | 2.2 |
| Compression Modulus Room Temperature - 20 Mpa KSW | % | DIN 28090-2 | 8 |
| Modulo di Compressione 150°C - 20 Mpa - 16 ore WSW | % | DIN 28090-2 | 3 |
| Creep Relaxation Room Temperature - 1 Mpa KRW | % | DIN 28090-2 | 15 |
| Compression Modulus 150°C - 20 Mpa - 16 hours WSW | % | DIN 28090-2 | 4 |
| Recovery | mm | DIN 28090-2 | 0.07 |
| Leakage Rate with nitrogen N2, 40bar, 32 N/mm2 | mg/s/m | DIN 28090-2 | < 0,01 |
| Leakage Rate with nitrogen N2, 40bar, 32 N/mm2 | cm3 /min | DIN 3535 | 0.02 |
| Compression Creep 150°C - 30 N/mm2 | N/mm2 | DIN 52913 | 16.5 |
| Compression Creep 175°C - 50 N/mm2 | N/mm2 | DIN 52913 | 29 |