SC 1100

FEATURES
  • Superior chemical resistance
  • Excellent resistance to deformation
  • No ageing
  • Good compressibility
  • High sealability
  • No water absorption
  • Non-flammable
  • Easy maintenance (assembling / disassembling)
Properties
PropertyUnitMethodValue
Pressure, maxbar/80
Temperature, min°C/-200
Temperature, max°C/260
P x T maxbar x °C/12,000
Densityg/cm3ASTM D7922.2
Compression Modulus Room Temperature - 20 Mpa KSW%DIN 28090-211
Creep Relaxation Roome Temperature - 1 Mpa KRW%DIN 28090-23
Compression Modulus 150°C - 20 Mpa - 16 hours WSW%DIN 28090-245
Creep Relaxation 150°C - 1 Mpa - 16 hours WRW%DIN 28090-24
RecoverymmDIN 28090-20.08
Leakage Ratemg/s/mDIN 28090-2
Leakage Rate (with Nitrogen)cm3 /minDIN 35350.01
Compression Creep 150°C - 30 N/mm2N/mm2DIN 5291314


Color: Light Blue

Sizes
Dimensions mmToll. mmThickness mmToll. mm
1500 x 1500+20 - 01,5 - 2,0 - 3,0+10% - 10%
PROPERTIES
PropertyUnitMethodValue
Pressure, maxbar/80
Temperature, min°C/-200
Temperature, max°C/260
P x T maxbar x °C/12,000
Densityg/cm3ASTM D7922.2
Compression Modulus Room Temperature - 20 Mpa KSW%DIN 28090-211
Creep Relaxation Roome Temperature - 1 Mpa KRW%DIN 28090-23
Compression Modulus 150°C - 20 Mpa - 16 hours WSW%DIN 28090-245
Creep Relaxation 150°C - 1 Mpa - 16 hours WRW%DIN 28090-24
RecoverymmDIN 28090-20.08
Leakage Ratemg/s/mDIN 28090-2
Leakage Rate (with Nitrogen)cm3 /minDIN 35350.01
Compression Creep 150°C - 30 N/mm2N/mm2DIN 5291314


Color: Light Blue

Sizes
Dimensions mmToll. mmThickness mmToll. mm
1500 x 1500+20 - 01,5 - 2,0 - 3,0+10% - 10%