Property | Unit | Method | Value |
---|---|---|---|
Pressure, max | bar | / | 80 |
Temperature, min | °C | / | -200 |
Temperature, max | °C | / | 260 |
P x T max | bar x °C | / | 12,000 |
Density | g/cm3 | ASTM D792 | 2.2 |
Compression Modulus Room Temperature - 20 Mpa KSW | % | DIN 28090-2 | 11 |
Creep Relaxation Roome Temperature - 1 Mpa KRW | % | DIN 28090-2 | 3 |
Compression Modulus 150°C - 20 Mpa - 16 hours WSW | % | DIN 28090-2 | 45 |
Creep Relaxation 150°C - 1 Mpa - 16 hours WRW | % | DIN 28090-2 | 4 |
Recovery | mm | DIN 28090-2 | 0.08 |
Leakage Rate | mg/s/m | DIN 28090-2 | |
Leakage Rate (with Nitrogen) | cm3 /min | DIN 3535 | 0.01 |
Compression Creep 150°C - 30 N/mm2 | N/mm2 | DIN 52913 | 14 |
Sizes | |||
---|---|---|---|
Dimensions mm | Toll. mm | Thickness mm | Toll. mm |
1500 x 1500 | +20 - 0 | 1,5 - 2,0 - 3,0 | +10% - 10% |
Property | Unit | Method | Value |
---|---|---|---|
Pressure, max | bar | / | 80 |
Temperature, min | °C | / | -200 |
Temperature, max | °C | / | 260 |
P x T max | bar x °C | / | 12,000 |
Density | g/cm3 | ASTM D792 | 2.2 |
Compression Modulus Room Temperature - 20 Mpa KSW | % | DIN 28090-2 | 11 |
Creep Relaxation Roome Temperature - 1 Mpa KRW | % | DIN 28090-2 | 3 |
Compression Modulus 150°C - 20 Mpa - 16 hours WSW | % | DIN 28090-2 | 45 |
Creep Relaxation 150°C - 1 Mpa - 16 hours WRW | % | DIN 28090-2 | 4 |
Recovery | mm | DIN 28090-2 | 0.08 |
Leakage Rate | mg/s/m | DIN 28090-2 | |
Leakage Rate (with Nitrogen) | cm3 /min | DIN 3535 | 0.01 |
Compression Creep 150°C - 30 N/mm2 | N/mm2 | DIN 52913 | 14 |
Sizes | |||
---|---|---|---|
Dimensions mm | Toll. mm | Thickness mm | Toll. mm |
1500 x 1500 | +20 - 0 | 1,5 - 2,0 - 3,0 | +10% - 10% |