TEKLEASE®

Guarniflon TEKLEASE® release film products have been specially formulated to suit a variety of individual composite process applications. Release films are used to separate and release the laminate from the vacuum stack following the cure of the composite component.

TEKLEASE® films are supplied both as perforated and unperforated to allow resin and volatiles to bleed out of the laminate and coloured for easy identification. The selection of a release film should be based on the resin system being used, the temperature and pressure of the cure cycle, the shape of the component to be cured and the amount of resin bleed that is required.

For example, release films that have higher elongations, will be more suitable for complex curvatures, though tailoring the film is recommended to ensure no bridging of the film occurs. It is important to remember that the mechanical performance of a film is dramatically affected by the presence of the perforations. Rolls of TEKLEASE® should be stored and handled in clean and dry conditions to prevent any contamination onto the final composite component.
Material Properties
CODEDESCRIPTIONMAX USE TEMP. (°C)ELONGATION AT BREAK (%)COLOUR
ET6200ETFE232350Blue / Clear
FE5000FEP260280Red
MRF1PTFE315250Natural
MRF2Modified PTFE315400Natural
Availability
CODETHICKNESS (μm)MAX WIDTH mm.ROLL LENGTH mm.OTHER
ET620015, 20, 25, 501220, 1530, 1780153Perforation available
FE500013, 20, 25, 501220, 1530, 1780153Perforation available
MRF125, 501220On requestPerforation available
MRF225, 501220On requestPerforation available
PROPRIETÀ MATERIALE
CODEDESCRIPTIONMAX USE TEMP. (°C)ELONGATION AT BREAK (%)COLOUR
ET6200ETFE232350Blue / Clear
FE5000FEP260280Red
MRF1PTFE315250Natural
MRF2Modified PTFE315400Natural
DISPONIBILITÀ
CODETHICKNESS (μm)MAX WIDTH mm.ROLL LENGTH mm.OTHER
ET620015, 20, 25, 501220, 1530, 1780153Perforation available
FE500013, 20, 25, 501220, 1530, 1780153Perforation available
MRF125, 501220On requestPerforation available
MRF225, 501220On requestPerforation available