SC 1400

FEATURES
  • Superior chemical resistance
  • Excellent resistance to deformation
  • No ageing
  • High compressibility
  • Superior sealability for a wide range of P and T
  • No water absorption
  • Non-flammable
  • Easy maintenance (assembling/disassembling)
  • Complies with FDA specifications
  • Certified by BAM (200°C, 25 bar)
  • In compliance with TA-Luft VDI 2240
Properties
PropertyUnitMethodValue
Pressure, maxbar/85
Temperature, min°C/-200
Temperature, max°C/260
P x T, maxbar x °C/12000
Densityg/cm3ASTM D7922.2
Compression Modulus Room Temperature - 20 Mpa KSW%DIN 28090-28
Modulo di Compressione 150°C - 20 Mpa - 16 ore WSW%DIN 28090-23
Creep Relaxation Room Temperature - 1 Mpa KRW%DIN 28090-215
Compression Modulus 150°C - 20 Mpa - 16 hours WSW%DIN 28090-24
RecoverymmDIN 28090-20.07
Leakage Rate with nitrogen N2, 40bar, 32 N/mm2mg/s/mDIN 28090-2< 0,01
Leakage Rate with nitrogen N2, 40bar, 32 N/mm2cm3 /minDIN 35350.02
Compression Creep 150°C - 30 N/mm2N/mm2DIN 5291316.5
Compression Creep 175°C - 50 N/mm2N/mm2DIN 5291329
PROPERTIES
PropertyUnitMethodValue
Pressure, maxbar/85
Temperature, min°C/-200
Temperature, max°C/260
P x T, maxbar x °C/12000
Densityg/cm3ASTM D7922.2
Compression Modulus Room Temperature - 20 Mpa KSW%DIN 28090-28
Modulo di Compressione 150°C - 20 Mpa - 16 ore WSW%DIN 28090-23
Creep Relaxation Room Temperature - 1 Mpa KRW%DIN 28090-215
Compression Modulus 150°C - 20 Mpa - 16 hours WSW%DIN 28090-24
RecoverymmDIN 28090-20.07
Leakage Rate with nitrogen N2, 40bar, 32 N/mm2mg/s/mDIN 28090-2< 0,01
Leakage Rate with nitrogen N2, 40bar, 32 N/mm2cm3 /minDIN 35350.02
Compression Creep 150°C - 30 N/mm2N/mm2DIN 5291316.5
Compression Creep 175°C - 50 N/mm2N/mm2DIN 5291329